Asphalt concrete

Mixture formulations

Mixing of asphalt and aggregate is accomplished in one of several ways:

• Hot mix asphalt concrete (commonly abbreviated as HMAC or HMA) is produced by heating the asphalt binder to decrease its viscosity, and drying the aggregate to remove moisture from it prior to mixing. Mixing is generally performed with the aggregate at about 300 °F (roughly 150 °C) for virgin asphalt and 330 °F (166 °C) for polymer modified asphalt, and the asphalt cement at 200 °F (95 °C). Paving and compaction must be performed while the asphalt is sufficiently hot. In many countries paving is restricted to summer months because in winter the compacted base will cool the asphalt too much before it is packed to the optimal air content. HMAC is the form of asphalt concrete most commonly used on highly trafficked pavements such as those on major highways, racetracks and airfields.

Superpave, short for "superior performing asphalt pavement," is a pavement system designed to provide longer lasting roadways. Key components of the system are careful selection of binders and aggregates, volumetric proportioning of ingredients, and evaluation of the finished product.

• Warm mix asphalt concrete (commonly abbreviated as WMA) is produced by adding either zeolites, waxes, or asphalt emulsions to the mix. This allows significantly lower mixing and laying temperatures and results in lower consumption of fossil fuels, thus releasing less carbon dioxide, aerosols and vapours. Not only are working conditions improved, but the lower laying-temperature also leads to more rapid availability of the surface for use, which is important for construction sites with critical time schedules. The usage of these additives in hot mixed asphalt (above) may afford easier compaction and allow cold weather paving or longer hauls.
• Cold mix asphalt concrete is produced by emulsifying the asphalt in water with (essentially) soap prior to mixing with the aggregate. While in its emulsified state the asphalt is less viscous and the mixture is easy to work and compact. The emulsion will break after enough water evaporates and the cold mix will, ideally, take on the properties of cold HMAC. Cold mix is commonly used as a patching material and on lesser trafficked service roads.
• Cut-back asphalt concrete is produced by dissolving the binder in kerosene or another lighter fraction of petroleum prior to mixing with the aggregate. While in its dissolved state the asphalt is less viscous and the mix is easy to work and compact. After the mix is laid down the lighter fraction evaporates. Because of concerns with pollution from the volatile organic compounds in the ligher fraction, cut-back asphalt has been largely replaced by asphalt emulsion. ^[2]
• Mastic asphalt concrete or sheet asphalt is produced by heating hard grade blown bitumen (oxidation) in a green cooker (mixer) until it has become a viscous liquid after which the aggregate mix is then added.

The bitumen aggregate mixture is cooked (matured) for around 6-8 hours and once it is ready the mastic asphalt mixer is transported to the work site where experienced layers empty the mixer and either machine or hand lay the mastic asphalt contents on to the road. Mastic asphalt concrete is generally laid to a thickness of around ³⁄₄–1 ³⁄₁₆ inches (20-30 mm) for footpath and road applications and around ³⁄₈ of an inch (10 mm) for flooring or roof applications.

In addition to the asphalt and aggregate, additives, such as polymers, and antistripping agents may be added to improve the properties of the final product.

• Natural asphalt concrete can be produced from bituminous rock, found in some parts of the world, where porous sedimentary rock near the surface has been impregnated with upwelling bitumen.
  
  

Asphalt concrete pavements—especially those at airfields—are sometimes called tarmac for historical reasons, although they do not contain tar and are not constructed using the macadam process.


Performance characteristics

Asphalt concrete has different performance characteristics in terms of surface durability, tire wear, braking efficiency and roadway noise. The appropriate asphalt performance characteristic is obtained by the traffic level amount in categories A,B,C,D,E, and friction coarse (FC-5). Asphalt concrete generates less roadway noise than Portland cement concrete surfacing, and is typically less noisy than chip seal surfaces. Tire noise effects are amplified at higher operating speeds. The sound energy is generated through rolling friction converting kinetic energy to sound waves. The idea that highway design could be influenced by acoustical engineering considerations including selection of surface paving types arose in the very early 1970s.^[3][4]


Asphalt concrete degradation and restoration

Asphalt deterioration can include crocodile cracking, potholes, upheaval, raveling, rutting, shoving, stripping, and grade depressions. In cold climates, freezing of the groundwater underneath can crack asphalt even in one winter (by frost heaving). Filling the cracks with bitumen can temporarily fix the cracks, but only proper construction, i.e. allowing water to drain away from under the road, can slow this process.

Factors that cause asphalt concrete to deteriorate over time mostly fall into one of two categories: Environmental factors and traffic loads. Often, damage results from combinations of factors in both categories.

Environmental factors include heat and cold, the presence of water in the subbase or subgrade soil underlying the pavement, and frost heaves.

High temperatures soften the asphalt binder, allowing heavy tire loads to deform the pavement into ruts. Paradoxically, high heat and strong sunlight also causes the asphalt to oxidize, becoming stiffer, less resilient and cracking. Cold temperatures can cause cracks as the asphalt contracts. Cold asphalt is also less resilient and more vulnerable to cracking.

Water trapped under the pavement softens the subbase and subgrade, making the road more vulnerable to traffic loads. Water under the road freezes and expand in cold weather, causing and enlarging cracks to form. In spring thaw, the ground thaws from the top down, so water is trapped between the pavement above and the still-frozen soil underneath. This layer of saturated soil provides little support for the road above, leading to the formation of potholes. This is more of a problem for silty or clay soils than sandy or gravelly soils. Some jurisdictions pass frost laws to reduce the allowable weight of trucks during the spring thaw season and protect their roads.

Traffic damage mostly results from trucks and busses. The damage a vehicle causes is proportional to the axle load raised to the fourth power ^[5], so doubling the weight an axle carries actually causes 16 times as much damage. Wheels cause the road to flex slightly, resulting in fatigue cracking, which often leads to crocodile cracking. Vehicle speed also plays a role. Slowly moving vehicles stress the road over a longer period of time, increasing ruts, cracking, and corrugations in the asphalt pavement.

Other causes of damage include heat damage from vehicle fires, or solvent action from chemical spills.

Prevention and repair of degradation

The life of a road can be prolonged through good design, construction and maintenance practices. During design, engineers measure the traffic on a road, paying special attention to the number and types of trucks. They also evaluate the subsoil to see how much load it can withstand. The pavement and subbase thicknesses are designed to withstand the wheel loads. Sometimes, geogrids are used to reinforce the subbase and further strengthen the roads. Drainage, including ditches, storm drains and underdrains are used to remove water from the roadbed, preventing it from weakening the subbase and subsoil.

Good maintenance practices center on keeping water out of the pavement, subbase and subsoil. Maintaining and cleaning ditches and storm drains will extend the life of the road at low cost. Sealing small cracks with bituminous crack sealer prevents water from enlarging cracks through frost weathering, or percolating down to the subbase and softening it. For somewhat more distressed roads, a chip seal or similar surface treatment may be applied. As the number, width and length of cracks increases, more intensive repairs are needed. In order of generally increasing expense, these include thin asphalt overlays, multicourse overlays, grinding off the top course and overlaying, in-place recycling, or full-depth reconstruction of the roadway.

It is far less expensive to keep a road in good condition than it is to repair it once it has deteriorated. This is why some agencies place the priority on preventive maintenance of roads in good condition, rather than reconstructing roads in poor condition. Poor roads are upgraded as resources and budget allow. In terms of lifetime cost and long term pavement conditions, this will result in better system performance. Agencies that concentrate on restoring their bad roads often find that by the time they've repaired them all, the roads that were in good condition have deteriorated.^[6]

Some agencies use a pavement management system to help prioritize maintenance and repairs.
RecyclingAsphalt concrete is often touted as being 100% recyclable. Very little asphalt concrete is actually disposed of in landfills.

Several in-place recycling techniques have been developed to rejuvenate oxidized binders and remove cracking, although the recycled material is generally not very water-tight or smooth and should be overlaid with a new layer of asphalt concrete. Cold in-place recycling mills off the top layers of asphalt concrete and mixes the resulting loose millings with asphalt emulsion. The mixture is then placed back down on the roadway and compacted. The water in the emulsion is allowed to evaporate for a week or so, and new hot-mix asphalt is laid on top.

Asphalt concrete that is removed from a pavement is usually stockpiled for later use as aggregate for new hot mix asphalt. This reclaimed material, commonly known by the acronym 'RAP' for recycled or reclaimed asphalt pavement, is crushed to a consistent gradation and added to the HMA mixing process. Sometimes waste materials, such as asphalt roofing shingles, crushed glass, or rubber from old tires, are added to asphalt concrete as is the case with rubberized asphalt, but there is a concern that the hybrid material may not be recyclable.


See also

• Free floating screed
• Plastic armour
• Tarmac
• Sealcoat

External links

Common types of asphalt distress


References

1. ^"Asphalt concrete cores for embankment dams". International Water Power and Dam Construction. Retrieved 3 April 2011.
2. ^Asphalt Paving Principles. Cornell Local Roads Program. 2003.
3. ^ John Shadely, Acoustical analysis of the New Jersey Turnpike widening project between Raritan and East Brunswick, Bolt Beranek and Newman, 1973
4. ^[1] C Michael Hogan, Analysis of Highway Noise, Journal of Soil, Air and Water Pollution, Springer Verlag Publishing, Netherlands, Vol. 2, Number 3 / September, 1973
5. ^ Equivalent Single Axle Load pavementinteractive.org/index.php
6. ^"Pavement Management Primer". Federal Highway Administration, U.S Department of Transportation. Retrieved 9/1/2011.

Convince yourself of our products for your applications.

We recommend the following products for your process medium:

ball valves and plug valves

gate valves